MPIF STD. 成分% 機械性質
Fe Cu C Ni Mo Mn Cr Sn Zn 密度 硬度
鐵系 F-0000 Bal, - 0-0.3 - - - - - - 6.1-6.7 HRF 40-60
FC-0205 Bal, 1.5-3.9 0.3-0.6 - - - - - - 6.0-7.1 HRB 37-72
FC-0205HT Bal, 1.5-3.9 0.3-0.6 - - - - - - 6.2-7.0 HRC 10-36
FC-0208 Bal, 1.5-3.9 0.6-0.9 - - - - - - 5.8-7.2 HRB 50-84
FC-0208HT Bal, 1.5-3.9 0.6-0.9 - - - - - - 6.1-7.1 HRC 20-43
FN-0205 Bal, 0-2.5 0.3-0.6 1-3 - - - - - 6.6-7.4 HRB 44-78
FN-0205HT Bal, 0-2.5 0.3-0.6 1-3 - - - - - 6.6-7.4 HRC 23-40
FN-0208 Bal, 0-2.5 0.6-0.9 1-3 - - - - - 6.7-7.4 HRB 63-88
FN-0208HT Bal, 0-2.5 0.6-0.9 1-3 - - - - - 6.7-7.4 HRC 26-42
FLN2C-4005 Bal, 1.3-1.7 0.4-0.7 1.5-2 0.4-0.6 0.05-0.3 - - - 6.7-7.4 HRB 81-93
FLN2C-4005HT Bal, 1.3-1.7 0.4-0.7 1.5-2 0.4-0.6 0.05-0.3 - - - 6.7-7.4 HRC25-40
FLNC-4408HT Bal, 1-3 0.6-0.9 1-3 0.65-0.95 0.05-0.3 - - - 6.8-7.2 HRC 21-30
FD-0205 Bal, 1.3-1.7 0.3-0.6 1.55-1.95 0.4-0.6 0.05-0.3 - - - 6.75-7.4 HRB 72-86
FD-0205HT Bal, 1.3-1.7 0.3-0.6 1.55-1.95 0.4-0.6 0.05-0.3 - - - 6.75-7.4 HRC 28-45
FD-0208 Bal, 1.3-1.7 0.6-0.9 1.55-1.95 0.4-0.6 0.05-0.3 - - - 6.75-7.25 HRB 80-90
FX-1008 Bal, 8-14.9 0.6-0.9 - - - - - - 7.3 HRB 89
FX-1008HT Bal, 8-14.9 0.6-0.9 - - - - - - 7.3 HRC 43
FX-2008 Bal, 15-25 0.6-0.9 - - - - - - 7.3 HRB 90
FX-2008HT Bal, 15-25 0.6-0.9 - - 0-2 - - - 7.3 HRC 36
不鏽鋼系 SS-303L Bal, - 0-0.03 8-13 - 0-2 17-19 - - 6.6-6.9 HRB 21-35
SS-304L Bal, - 0-0.03 8-12 - 0-2 18-20 - - 6.6-6.9 HRB 30-45
SS-316L Bal, - 0-0.03 10-14 2-3 0-1 16-18 - - 6.6-6.9 HRB 20-45
SS-410L - - 0-0.03 - - - 11.5-13.5 - - 6.9 HRB 45
銅系 CT-1000 - 87-.5-90.5 - - - - - 9.5-10.5 - 7.2 HRH32
CZ-1000 - 88-91 - - - - - - Bal. - -